Haynes R-41  alloys have good creep and oxidation resistance, and are formed in different  shapes. They are classified into three types such as cobalt-based,  nickel-based, and iron-based super alloys. They have the ability to function at  very high temperatures and under mechanical stress.

They can be  strengthened by performing solid-solution hardening, work hardening, and  precipitation hardening. The cobalt-based and nickel-based super alloys can be  in the form of wrought or cast based on their application or composition.

Haynes(r) R-41  is a wrought nickel base high temperature and strength alloy. Double aging and  solution heat treating are performed at low temperatures in order to increase  its strength.

Product Description

Haynes R-41 Machinability:

Haynes(r) R-41  can be machined using conventional methods which are used for iron-based  alloys. Commercial coolants are used for performing machining operations.  Water-based coolants are used for performing high-speed operations such as  milling, grinding or turning. Heavy lubricants are preferred for tapping,  drilling, boring or broaching.

Haynes R-41 Forming:

Haynes(r) R-41 can be formed using all conventional  techniques.

Haynes R-41 Welding:

Haynes(r) R-41 is welded using gas-tungsten  arc welding, gas metal-arc welding, shielded metal-arc welding and  submerged-arc welding methods.

Haynes R-41 Heat Treatment:

Haynes(r) R-41 is heat treated by annealing  at 1080°C (1975°F) for 4 h followed by cooling. After this process, aging heat  treatment is done at 760°C (1400°F) for 16 h followed by cooling.

Haynes R-41 Heat Forging:

Haynes(r) R-41 can be forged in the  solution annealed condition.

Haynes R-41 Cold Working:

Haynes(r) R-41 is cold worked using  standard tooling.
 Haynes R-41 Annealing:

Haynes(r) R-41 is annealed at 1066 to  1080°C (1950 to 1975°F) for 4 h followed by cooling.

Haynes R-41 Aging:

Haynes(r) R-41 is aged at 760°C (1400°F)  for 16 h followed by cooling.

Haynes R-41 Hardening:

Haynes(r) R-41 can be hardened only by cold  working.
 
 Product Application

Haynes R-41  Application：

Haynes(r) R-41 is used in high temperature  and strength environments which require high oxidation resistance. It is also  used in aircraft, gas turbine and land/marine, applications.

ur Service

• Spot delivery, including delivering small batches of goods

• Provide wide-range and complete materials series products

• Cutting plates, including complex shapes of materials and special  processing and disposal

• Cutting bars and strips

• Our application technology expert provide the best material and  recommendation

• One-stop service